COC德国TOPAS 6013M-07透镜专用料是一种光学级透明共聚物,由东莞市高创塑胶原料有限公司销售。该材料具有以下物性表参数:
1. **物理性能**:
- **密度**:1.01 g/cm³ (ISO 1183)
- **溶化体积流率M VR**:
- 190℃/2.16 kg: 2.00 cm³/10min (ISO 1133)
- 230℃/2.16 kg: 11.0 cm³/10min (ISO 1133)
- **吸水率**(饱和,23℃): 0.010 % (ISO 62)
2. **机械性能**:
- **拉伸模量**:
- MD (机器方向): 2100 MPa (ISO 527-3)
- TD (横向): 1800 MPa (ISO 527-3)
- **拉伸应力**:
- MD (断裂): 55.0 MPa (ISO 527-3)
- TD (断裂): 52.0 MPa (ISO 527-3)
- **伸长率**:
- MD (断裂): 3.4 % (ISO 527-3)
- TD (断裂): 3.4 % (ISO 527-3)
3. **水气透过率**:38℃,90% RH条件下为0.850 gmm/m²/atm/24 hr (ISO 15106-3)
4. **热性能**:
- **玻璃转化温度**: 78.0 ℃ (ISO 11357-2)
TOPAS® COC 6013M-07还具有以下特性:
- **颜色**:符合ISO(JIS)材质表示,等级为>COC<,表示具有优质外观性。
- **MVR (熔体流动速率)**:在260℃, 2.16kg条件下为13 cm³/10min (ISO 1133)。
- **拉伸弹性模量**:2900 MPa (ISO 527-2/1A)。
- **拉伸破坏强度**:63 MPa (ISO 527-2/1A)。
- **拉伸破坏伸率**:2.6 % (ISO 527-2/1A)。
- **弯曲强度** 和 **弯曲模量**:具体数值未提供。
- **简支梁冲击强度**:
- 无缺口: 14 kJ/m² (ISO 179/1eU)
- 有缺口、23℃: 1.7 kJ/m² (ISO 179/1eA)
- **玻璃化转变温度**:142 ℃ (ISO 11357)。
- **负荷变形温度**:130 ℃ (ISO 75-1,2)。
- **光线透过率**:91 % (2mm厚,ISO 13468-1)。
- **折射率**:1.53 (ISO 489)。
TOPAS® COC 6013M-07因其高纯度、高刚性、透明性、耐热性以及良好的耐化学性,适用于医疗、包装、电子部件等多个领域,特别是在需要高透明度和耐化学性的场合。此外,TOPAS® COC还具有良好的水蒸汽阻隔性和低介电常数,易于回收和热成型,提供了广泛的应用可能性。